I.INTRODUCTIONUnlike normal incidence reflective optics, reflective optical elements for X-rays are designed to reflect at shallow incident angles. In this configuration, the collecting area is a small fraction of the geometric area; therefore several mirrors have to be nested to increase the effective area of the telescope, so that the optical modules dominate the mass budget of the instrument payload. Future generation X-ray telescopes, like ATHENA [1], need to be realized with lightweight optics providing both large effective area (Aeff = 2 m2 at 1 keV) and high angular resolution (5 arcsec HEW, Half Energy Width). Materials lighter than Nickel (as used for XMM) or thick Zerodur glass (as used for Chandra) are therefore to be considered as candidates for lightweight, high-performances optics. A new technology, different from the replica process of the XMM Nickel shells or the direct polishing of the Chandra thick glasses, has to be developed. The Brera Astronomical Observatory (INAF-OAB) is developing the Slumped Glass Optics (SGO) technology to manufacture the modular elements required for the optics of the ATHENA mission. In our laboratories we form thin glasses (0.4 mm thin) by direct hot slumping, assisted by pressure, replicating the shape of a cylindrical mould. The formed foils are then stacked into Wolter-I configuration via a dedicated Integration Machine (IMA), to form the X-ray Optical Unit (XOU), the basic element of the telescope. II.SLUMPED GLASS OPTICS TECHNOLOGYThe SGO technology is based on thin glasses curved by hot slumping with a replica process and then integrated in the Wolter I configuration on a dedicated equipment. We are working on this technology since 2009. The research was supported until June 2013 by the European Space Agency (ESA) and proceeded with the collaboration of several institutes and Italian companies: Max Planck Institut für Extraterrestrische Physik (MPE, Garching, Germany), BCV-Progetti (Milano, Italy), ADS-International (Lecco, Italy), and Media Lario Technologies (Bosisio Parini, Italy). The study is still pursued to optimize our SGO technology. Each individual glass of the XOU has to be curved in a furnace with a proper thermal cycle fit to enable a good surface roughness and the optimal curvature. In our laboratories we have developed a slumping process assisted by pressure [2], whose setup has been patented (TO2013A000687, 12/08/2013). In Fig 1 we show the furnace, the slumping mould, the glass and the muffle to enable the pressure application. The glass, slumped to a size larger than the mould, also acts as a membrane to divide the muffle chamber in two parts: the bottom part has a lower pressure, which drags the glass toward the mould surface and forces it into contact. The slumped glass has then to be trimmed to the final dimension, 200 × 200 mm. The typical thickness of the glass is 0.4 mm. The slumped glasses are characterized in shape with a Long Trace Profilometer for 1-D profiles and with the Characterization Universal Profilometer (CUP), developed at our laboratories, for 2-D maps [3]. Moreover, their surface roughness is characterized with an Atomic Force Microscope (AFM), a WYKO Phase Shift Interferometer and a Micro-Finish Topographer (MFT) [4]. The slumped glasses have cylindrical shape and they have to be integrated into the final Wolter-I configuration. We obtain this step via an ad-hoc designed and developed machine named Integration Machine (IMA) (Fig.2). The glasses are stacked and glued with glass ribs which, in addition to keep the mirror aperture clear by a proper spacing, endow the structure with mechanical stiffness, and eventually freeze into the glasses the Wolter-I profiles of the integration mould, thus correcting for residual low frequency error profiles [5]. Finite Element Analysis was performed with the ANSYS software [6] to evaluate the capability of the process to correct the initial errors at different spatial wavelengths: the basic result is that long-period errors are corrected almost entirely, whereas errors over a few cm scale remain almost unchanged after the integration. An opto-mechanical study for different types of materials and different XOU design was recently performed fulfilling the requirements specified by the ATHENA mission [7]. The study, already performed for the IXO [6] X-ray telescope with a 20 m focal length and an effective area of 3 m2 at 1 keV, was reviewed for a 12 m focal length telescope, with 2 m2 effective area at 1 keV, the characteristics of ATHENA. In Fig. 3 we show a possible distribution of the XOUs inside the optical module structure. III.STATE-OF-THE-ART PERFORMANCESThe first prototype of SGO, the Proof of Concept #1 (PoC#1), was produced using 0.4 mm thick Schott D263 glass foils, slumped on a Pt-coated Fused Silica cylindrical mould [8]. The resulting Half Energy Width (HEW) was 80 arcsec, affected by a high surface roughness, because of the utilization of a metal membrane for pressure application and poorly shaped integration moulds in Metapore, a material difficult to figure precisely. The subsequent prototype, XOU-BB (X-Ray Optical Unit Bread Board) was then realized with D263 glass foils slumped on moulds of different materials and using different settings for the application of pressure [2]. Its main goal was to manufacture a complete optical unit model of the IXO optical system, demonstrating in particular the capability of stacking of plate pairs with the IMA. A later prototype (PoC#2) was produced with Schott AF32 glasses slumped on a Zerodur K20 mould; a better matching of the Coefficient of Thermal Expansion (CTE) of the two materials has enabled smaller errors in the slumped glass shape. The glasses were then integrated using newly procured BK7 integration moulds, with much more accurate Wolter-I profiles with respect to the previous Metapore moulds. These modifications have allowed the complete module to reach a HEW of ~ 22 arcsec and the better plate pair a HEW of ~ 20 arcsec, directly measured in-focus at 0.27 keV at the PANTER facility [9]. Finally, a last prototype (PoC#3) was realized with Corning Eagle glass foils slumped on a newly procured Zerodur K20 slumping mould, with better surface roughness with respect to the previous one [10]. Despite the overall HEW higher with respect to the PoC#2, the X-ray analysis, performed at the PANTER/MPE facility in pencil beam mode, showed a best HEW value, in a portion of the module, of 5.5 arcsec at 0.27 keV (Fig. 4) [9]. Moreover, the impact of the roughness in the 0.27-1.49 keV range was considerably reduced with respect to the previous prototypes, denoting a better surface roughness. Table 1:Description of the prototypal models realized @ INAF-OAB
The detailed results for the last two prototypes can be found elsewhere [9]: this paper concentrates on presenting the currently achieved know-how and performance of the hot slumping technology @ INAF-OAB. IV.THE DIRECT HOT SLUMPING ASSISTED BY PRESSUREThe hot slumping is a replica process in which the temperature is brought high enough to soften the glass and slump it over the mould; when the glass is brought back to room temperature, it retrieves its solid state and thereby copies the mould profile. If the surface of the glass in contact with the mould is the optical one (direct approach) the roughness of the mould surface is replicated on the glass side, at least partially. On the other hand, if the surface in contact with the mould is the non-optical one (indirect approach), all the glass thickness variations are transferred to the optical surface. In both cases, the quality of the X-ray telescope is degraded and those effects have to be minimized. Different glass types can be used. Schott D263 glasses were used for instance at the NASA-Goddard laboratories and Columbia University (USA) for the NuSTAR optics [11]; they were also used in an early phase of our research [8] and are still currently used in the Max Planck Institut für Extraterrestrische Physik (MPE, Germany) [12]. The Schott AF32 glass type was then used in our laboratories. More recently, the Corning Eagle XG glass was used, as Schott discontinued the production of the AF32 glass in the size necessary for our setup. A mould in Zerodur K20 was selected, as it does not require an anti-sticking layer (unlike Fused silica, Silicon or Silicon Carbide). The good coupling of the CTE of the glass and the mould is a key factor for the optical quality of the slumped glass (CTEK20 = 2.0 10-6/°K, CTED263 = 7.2 10-6/°K, CTEAF32 = 3.2 10-6/°K, CTEEagle = 3.17 10-6/°K), as it avoids the shear of the optical surface on the mould when the temperature is decreased, thereby reducing errors in the centimeter spatial wavelengths. These types of errors are expected to be present on the glass surface, when the glass is in contact with the mould [13], and they have to be minimized as, unlike low frequency errors, they are not corrected by the integration procedure. Another key factor is the applied pressure, that helps reducing the mid frequency errors. The resulting CUP maps of two glasses slumped with pressure of 50 g/cm2 and 20 g/cm2 are compared in Fig 5: the higher mid frequency errors content is evident in the glass slumped with lower pressure (Fig. 5, right). Actually, a trade-off for the pressure value has to be found, as higher pressure values reduce the mid-frequencies but at the same time increase the high frequency errors. The Zerodur K20 surface is in fact crowded with peaks that degrade the glass surface in contact with the mould [14]. As the surface roughness of the K20 mould used for the production of the PoC#2 was degraded after several slumping cycles, a new Zerodur K20 mould was purchased (named hereafter MK20-20). Improved surface roughness of the slumped glasses was obtained with this mould [10]. Still the pressure value could not be set higher than the standard 50 g/cm2, in order to not degrade the slumped glass surface. In Fig. 6, the roughness of a Eagle glass, slumped with direct approach at pressure of 50 g/cm2 (blue lines), is compared with the roughness of the MK20-20 slumping mould (red/orange lines). It appears that, in the 0.1-100 μm spatial wavelength region, the roughness of the mould is only slightly replicated on the glass optical surface. In contrast, in the mm range, the roughness of the glass is comparable to the one of the mould. In Fig. 6 we also traced the PSD of the Eagle glass before being formed. In order to avoid HEW degradation at energies higher than 1 keV and up to 5 keV, we should aim at preserving the roughness of the glass optical surface as closer as possible to that PSD, which will represent our target value for the surface roughness, especially in the mm range. In section V we outline the work ongoing for the indirect slumping, both on Zerodur K20 and Silicon Nitride as slumping moulds, aiming at preserving the native glass roughness for the optical glass surface. Finally, we show the CUP maps obtained on two glasses slumped on the new MK20-20 (Fig. 7). The E16 was one of the two glasses integrated in the PoC#3. It was slumped on MK20-20 after two preliminary slumping cycles that suffered from air entrapping in the central region and most likely asymmetric deformation of the K20 material [10]. Therefore, this glass shows residual errors in the central region (Fig.7 left/bottom) that degrade the resulting HEW (Fig.4). To investigate the K20 deformation on subsequent slumping cycles, other glasses were slumped on the same mould with the same process parameters. The glass, shown in the right side of Fig. 7, was slumped after 5 slumping cycles, giving better results in terms of mid frequency errors. It was also slumped with a prolonged soaking time, thus affecting the surface roughness. An optimal value needs to be found also for the soaking time. Regarding the deformation of the K20 material, Silicon Nitride is considered a very promising alternative material, because it does not exhibit deformation after a slumping cycle with pressure (see section V). V.RECENT PROGRESS OF SGOAfter demonstrating the capabilities of the SGO technology for high-resolution X-ray space telescopes, we considered the possibility to improve the performances bypassing the limits of our setup. Namely, two limits were considered key factors: the Zerodur K20 deformation and the degradation of the optical surface on the direct slumping. The research on the Silicon Nitride, as a material for the slumping moulds, was driven by three key points: a higher rigidity with respect to the Zerodur K20 (Young’s Modulus for Si3N4 = 300 GPa, for K20 = 84.7 GPa), a better matching of the CTE with the one of the glass (CTESi3N4 = 3.4×10-6/°K, CTEEagle = 3.17 10-6/°K), and a higher thermal conductivity (k) with respect to the Zerodur K20 (kSi3N4 = 33 W/mK, kK20 =1.63 W/mK). We hence have purchased flat sample moulds of Silicon Nitride. Several slumping tests, with increasing temperature and pressure, were performed on a sample to ascertain the absence of sticking. No sticking ever occurred, proving this material as a good candidate for the slumping technique. Moreover, the increased rigidity of the Si3N4 with respect to the Zerodur K20 was shown by performing profiles measurements on the Si3N4 diameter before and after the slumping with standard process parameters (Fig. 9). No deformation occurred on Si3N4, whilst we experienced it on Zerodur K20 mould. The rigidity of this material makes also possible to produce a cylindrical slumping mould thinner than the mould in K20, thus reducing the cost of the mould production: FEA showed that a negligible deformation for a cylindrical mould with dimension 250 x 250 mm and radius of curvature of 1 m, in our working conditions, can be obtained with mould thickness of 50 mm for the K20 whilst 32 mm for the Si3N4. From the roughness point of view, the Silicon Nitride sample moulds were very rough, with rms@WYKO = 207 Å (Fig. 11), as no special attention was paid to the polishing of the mould in this first phase of the research. The surface was crowded with peaks (Fig. 10.c) and this entails a very poor quality of the slumped glass surface in contact with the mould (Fig.10-a). Still, the slumped glass surface not in contact with the mould (indirect approach) is almost comparable to the pristine glass (Fig.10-b). In Fig. 11, the roughness of the Si3N4 slumping mould, and the ones of the slumped Eagle glass, considering both direct and indirect approaches are compared. The polishing capability on the Si3N4 will be investigated in a later phase. We also started tests on the indirect slumping by using a mould in Zerodur K20 with concave cylindrical shape and a 2 m radius of curvature. Despite the low quality of the mould surface, we consider this a good test to check our setup with pressure application on cylindrical moulds also for the indirect slumping. Fig. 12.c shows the patterns present on the mould surface reproduced on the optical side of the slumped D263 glass, proving that the setup was correctly driving the glass in contact with the mould. The process parameters were the same as for the direct approach and yielded a longitudinal PV of about 40 μm, to be compared with the 8 μm longitudinal error of the slumping mould. VI.CONCLUSION AND OUTLOOKThe SGO technology developed at INAF-OAB has considerably advanced since 2009. Several prototypes have been already realized proving that the hot slumping technology assisted by pressure and our integration concept are a key combination for the realization of lightweight X-ray telescopes of future generation. To date the best result, on the overall prototype, was obtained with AF32 glasses slumped on Zerodur K20 (PoC#2), returning 22 arcsec at 0.27 keV. Improvement on the roughness was obtained purchasing a new slumping mould in Zerodur K20 and the best region of the PoC#3 prototype (produced with Eagle glasses) was 5.5 arcsec at 0.27 keV, with an overall increment of 1 arcsec on all the prototype by increasing the energy to 1.49 keV. We are now working on alternative solutions for the observed deformation of the Zerodur K20 mould and the still high roughness of the slumped glasses with the direct approach. Si3N4 seems to be a promising material, as it does not stick to the glass at our slumping temperature and pressure, as Zerodur K20, but in addition it does not deform with the slumping cycles, owing to its higher stiffness. We have performed preliminary slumping tests of Eagle glasses over a flat sample of Si3N4 and the results show that, despite the very high roughness of the mould surface, the glass surface not in contact with the glass has roughness values comparable with the one of pristine glasses. We have proven, both with the flat Si3N4 sample and with a concave Zerodur K20 mould, that our setup for pressure application is suitable also for the indirect approach. For the next steps, we will work in parallel with the direct and indirect approach. A research on the hot slumping for normal incidence mirrors in also planned: a first prototype was already produced at our laboratories [15] combining the good optical performances achievable on optics produced by means of the hot slumping technique with the lightweight and stiffness of the foamed material in sandwich-like structures. REFERENCESNandra, K., Barcons, X., Barret, D., Fabian, A., den Herder, J.W., Piro, L., Watson, M.,
“Athena: The Advanced Telescope for High Energy Astrophysics,”
Mission proposal, http://www.the-athena-x-ray-observatory.eu Google Scholar
Ghigo, M., Basso, S., Borsa, F., Bavdaz, M., Citterio, O., Civitani, M.,
“Development of high angular resolution x-ray telescopes based on slumped glass foils,”
in Proc. SPIE,
84430R
(2012). Google Scholar
M. M. Civitani, M. Ghigo, O. Citterio, P. Conconi, D. Spiga, G. Pareschi, L. Proserpio,
“3D characterization of thin glass x-ray mirrors via optical profilometry,”
in Proc. SPIE,
78030L
(2010). Google Scholar
Parks, R.E.,
“MicroFinish Topographer: surface finish metrology for large and small optics,”
in Proc. SPIE,
81260D
(2011). Google Scholar
Civitani, M., Basso, S., Citterio, O., Conconi, P., Ghigo, G., Pareschi,
“Accurate integration of segmented X-ray optics using interfacing ribs,”
Optical engineering, 52
(9), 091809
(2013). Google Scholar
Parodi, G., Martelli, F., Basso, S., Citterio, O., Civitani, M., Conconi, P.,
“Design of the IXO optics based on thin glass plates connected by reinforcing ribs,”
in Proc. SPIE,
81470Q-1
(2011). Google Scholar
Basso, S., Buratti, E., Civitani, M.M., Pareschi, G., Salmaso, B., Spiga, D., Tagliaferri, G., Eder, J.,
“A high resolution large x-ray mission based on thin glass: optomechanical design,”
in Proc SPIE,
91444C
(2014). Google Scholar
Proserpio, L., Ghigo, M., Basso, S., Conconi, P., Citterio, O., Civitani, M.,
“Production of the IXO glass segmented mirrors by hot slumping with pressure assistance: tests and results,”
in Proc. SPIE,
81470M
(2011). Google Scholar
Civitani, M., Basso, S., Ghigo, G., Pareschi, G., Salmaso, B., Spiga, D.,
“X-ray Optical Units made of glass: achievements and perspectives,”
in Proc. SPIE,
914416
(2014). Google Scholar
Salmaso, B., Basso, S., Brizzolari, C., Civitani, M.M., Ghigo, M., Pareschi, G.,
“Production of thin glass mirrors by hot slumping for X-ray telescopes: present process and ongoing development,”
in Proc SPIE,
91512W
(2014). Google Scholar
Koglin, J.E., An, H., Barrière, N., Brejnholt, N.F., Christensen, F.E., Craig, W.W, Hailey, C.J.,
“First results from the ground calibration of the NuSTAR flight optics,”
in Proc. SPIE,
81470J
(2011). Google Scholar
Winter, A., Breunig, E., Burwitz, V., Friedrich, P., Hartner, G.,
“Light-weight glass mirror systems for future x-ray telescopes,”
in Proc. SPIE,
88610Q
(2013). Google Scholar
Jimenez-Garate, M. A., Hailey, C. J., Craig, W. W., Christensen, F. E.,
“Thermal forming of glass microsheets for x-ray telescope mirror segments,”
Applied Optics, 42 4
(2003). Google Scholar
Salmaso, B., Bianco, A., Citterio, O., Pareschi, G., Pariani, G., Proserpio, L.,
“Micro-roughness improvement of slumped glass foils for X-ray telescopes via dip coating,”
in Proc. SPIE,
(2013). Google Scholar
Canestrari, R., Ghigo, M., Pareschi, G., Basso, S., Proserpio, L.,
“Investigation of a novel slumping technique for the manufacturing of stiff and lightweight optical mirrors,”
in Proc. SPIE,
7018D
(2008). Google Scholar
|