Optical contacting of low-expansion materials

G. Kalkowski; S. Risse; C. Rothhardt; M. Rohde; R. Eberhardt

doi:10.1117/12.894382

27 September 2011 Optical contacting of low-expansion materials

G. Kalkowski, S. Risse, C. Rothhardt, M. Rohde, R. Eberhardt

Proceedings Volume 8126, Optical Manufacturing and Testing IX; 81261F (2011) https://doi.org/10.1117/12.894382
Event: SPIE Optical Engineering + Applications, 2011, San Diego, California, United States

Abstract

We report on optical contacting or "direct bonding" of glass to glass for optical and precision engineering applications. Fused silica (SiO2) and ultra-low-expansion (ULE) glass materials with low and extremely low coefficients of thermal expansion, respectively, were investigated. Large glass wafers of up to 150 mm diameter and about 1.5 mm thickness were bonded to each other and to plane glass substrates of up to 20 mm thickness. Successful bonding was achieved after extensive chemical cleaning and low pressure plasma surface activation, using a commercial wafer bonding equipment. High quality (optically transparent) bonds with a very low fraction of aerial defects were obtained at low bonding temperatures of about 250 °C, by applying compressive forces of several tens of kN in a high vacuum environment. Typically, only small unbound locations occurred at the rim, where insufficient pressure had been applied in the bonding process. Bonding strengths were estimated from destructive "razor-blade" testing of bonded wafer pairs, resulting in bond energies up to about 2 J/m². For surface activation, Nitrogen-plasma was tested in comparison to Oxygen-Plasma without significant differences. However, ULE wafers were found to bond much stronger than fused silica wafers under nominally identical bonding conditions. An exemplary "sandwich" structure was generated from ULE materials by bonding wafers from both sides to a core structure, obtained by perforating a massive plane plate with bore holes. This illustrates possible use in light-weight and stiff construction for high precision opto-mechanical applications.

Citation Download Citation

G. Kalkowski, S. Risse, C. Rothhardt, M. Rohde, and R. Eberhardt "Optical contacting of low-expansion materials", Proc. SPIE 8126, Optical Manufacturing and Testing IX, 81261F (27 September 2011); https://doi.org/10.1117/12.894382

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available