The influence of atmospheric species on the degradation of aluminum doped zinc oxide and Cu(In,Ga)Se2 solar cells

Mirjam Theelen; Christopher Foster; Supratik Dasgupta; Zeger Vroon; Nicolas Barreau; Miro Zeman

doi:10.1117/12.2061330

8 October 2014 The influence of atmospheric species on the degradation of aluminum doped zinc oxide and Cu(In,Ga)Se₂ solar cells

Mirjam Theelen, Christopher Foster, Supratik Dasgupta, Zeger Vroon, Nicolas Barreau, Miro Zeman

Author Affiliations +

Proceedings Volume 9179, Reliability of Photovoltaic Cells, Modules, Components, and Systems VII; 91790K (2014) https://doi.org/10.1117/12.2061330
Event: SPIE Solar Energy + Technology, 2014, San Diego, California, United States

Abstract

Aluminum doped zinc oxide (ZnO:Al) layers were exposed to the atmospheric gases carbondioxide (CO₂), oxygen (O₂), nitrogen (N₂) and air as well as liquid H₂O purged with these gases, in order to investigate the chemical degradation behavior of these layers. The samples were analyzed by electrical, compositional and optical measurements before, during and after exposure to these conditions in order to follow the degradation behavior of these layers in time. We have shown that ZnO:Al layers degraded in the presence of a mixture of H₂O and CO₂. Individually, CO₂does not impact the degradation at all during the tested period, while the individual impact of H₂O is small. However, when CO₂ is also present, the concentration of OH increases greatly in the bulk and even more at the air/ZnO:Al and the ZnO:Al/glass interfaces. Carbon based species are then also present, indicating that Zn5(OH)6(CO3)2 is also formed at the grain boundaries. The degradation of ZnO:Al was accompanied by the occurrence of holes in the ZnO:Al layer near the ZnO:Al/glass interface. The impact of gaseous O₂ as well as water purged with N₂ and O₂ on ZnO:Al degradation is very small. Complete Cu(In,Ga)Se₂ solar cells were also exposed to unpurged liquid H₂O and H₂O purged with CO₂, O₂, N₂ and air. The samples exposed to H₂O purged with air and CO₂ showed a rapid decrease in efficiency after approximately 180 hours of exposure. This efficiency decrease is mainly driven by a very rapid decrease in current density and an increase in series resistance.

Citation Download Citation

Mirjam Theelen, Christopher Foster, Supratik Dasgupta, Zeger Vroon, Nicolas Barreau, and Miro Zeman "The influence of atmospheric species on the degradation of aluminum doped zinc oxide and Cu(In,Ga)Se₂ solar cells", Proc. SPIE 9179, Reliability of Photovoltaic Cells, Modules, Components, and Systems VII, 91790K (8 October 2014); https://doi.org/10.1117/12.2061330

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available